This is extremely easy to use and just requires a stainless steel vessel and your kitchen stove. It gives a classic rust blue finish and is not caustic. If you are working with silver or lead soldered pieces there are no bad consequences and gives a nice blue finish.

“Bluing is a passivation process in which steel is partially protected against rust, and is named after the blue-black appearance of the resulting protective finish. True gun bluing is an electrochemical conversion coating resulting from an oxidizing chemical reaction with iron on the surface selectively forming magnetite (Fe₃O₄), the black oxide of iron. Black oxide provides minimal protection against corrosion, unless also treated with a water-displacing oil to reduce wetting and galvanic action.

In comparison, rust, the red oxide of iron (Fe₂O₃), undergoes an extremely large volume change upon hydration; as a result, the oxide easily flakes off causing the typical reddish rusting away of iron. “Cold”, “Hot”, “Rust Blue” and “Fume Blue” are oxidizing processes simply referred to as bluing.

“Cold” bluing is generally a selenium dioxide based compound that colors steel black, or more often a very dark gray. It is a difficult product to apply evenly, offers minimal protection and is generally best used for small fast repair jobs and touch-ups.

The “Hot” process, is an alkali salt solution referred to as “Traditional Caustic Black” that is typically done at an elevated temperature 275°F (135°C) to 310°F (154.44°C) . This method was adopted by larger firearm companies for large scale, more economical bluing. It does provide good rust resistance which is of course improved with the use of oil.

“Rust Bluing” and “Fume Bluing” provide the best rust and corrosion resistance as the process continually converts any metal that is capable of rusting into (Fe₃O₄). Treating with an oiled coating enhances the protection offered by the bluing. This process is also the only process safely used to re-blue vintage shotguns. Many double barreled shotguns are silver brazedtogether and many of the parts are attached by that method also. The higher temperatures of the other processes as well as their caustic nature can weaken the brazed joints and make the gun hazardous to use.

Bluing is most commonly used by gun manufacturers, gunsmiths and gun owners to improve the cosmetic appearance of, and provide a measure of corrosion resistance to, their firearms. It was also used by machinists, who protected and beautified tools made for their own use. Bluing also helps to maintain the metal finish by resisting tangential scratching, and also helps to reduce glare to the eyes of the shooter when looking down the barrel of the gun. All blued parts still need to be properly oiled to prevent rust. Bluing, being a chemical conversion coating, is not as robust against wear and corrosion resistance as plated coatings, and is typically no thicker than 2.5 micrometres (0.0001 inches). For this reason, it is considered not to add any appreciable thickness to precisely-machined gun parts.

New guns are typically available in blued finish options offered as the least-expensive finish, and this finish is also the least effective at providing rust resistance, relative to other finishes such as Parkerizing or hard chrome plating or nitriding processes like Tenifer.

Bluing is also used for providing coloring for steel parts of fine clocks and other fine metalwork.

Bluing is often a hobbyist endeavor, and there are many methods of bluing, and continuing debates about the relative efficacy of each method.

Historically, razor blades were often blued steel. A non-linear resistance property of the blued steel of razor blades, foreshadowing the same property that would later be discovered in semi-conductor diode junctions, along with the ready availability of blued steel razor blades, led to the use of razor blades as a detector in the crystal set AM radios which were often built by soldiers during World War II.^[1]“

Moving under any circumstances is difficult…… moving an entire machine shop without heavy equipment machinery movers is an undertaking.  Sue and I are relocating to Albuquerque, NM  - so far we have three pods (one and a half already loaded)  and will probably need a 26 ft. truck.  The pods are necessary because they can be loaded at ground level -a requirement when you’re moving a 3200# lathe by hand.  Yesterday Ray Del Rio and Gary Elisio’s son Jeremy (dad was in Phoenix this weekend shooting) helped move the lathe.  This is why I’m not in Phoenix this weekend. Today Mike Tuck helped secure the lathe to the inside of the pod and move lots of other stuff.  Any able bodies in  Southern California are more than welcome to join the fun!